ASTM A387 Grade 22 Class 2 / ASME SA387 Grade 22 Class 2
In this section:chrome moly steel | A387 Grade 11 Class 2 | A387 Grade 12 Class 2 | A387 Grade 22 Class 2
A387 Grade 5 Class 2 | A387 Grade 91 Class 2 | A387 Grade 9 Class 2
A387 Grade 22 Class 2 is a grade of chromium-molybedenum alloy intended primarily for use in welded boilers and pressure vessels which are designed for use in raised temperature service.
With excellent heat resistance and anti corrosive/oxidation qualities, this steel grade is ideal for use in the chemical, oil and gas industry.
ASTM / ASME Specification:
- ASTM A387 Grade 22 Class 2
- ASME SA387 Grade 22 Class 2
Equivalents
| BS | EN | ASTM/ASME | DIN |
| 622-515B | 10 CRMO910 | A387-22-2 | 10 CRMO910 |
Specifications
Chromium & Molybdenum content (according to the ASTM specification):
| Designation | Nominal Chromium Content (%) |
Nominal Molybdenum Content (%) |
| A387 Grade 22 | 2.25% | 1.00% |
Tensile Requirements for Class 2 Plates
| Designation: | Requirement: | Grade 22 |
| A387 Grade 22 | Tensile strength, ksi [MPA] | 75 to 100 [515 to 690] |
| Yield strength, min, ksi [MPa]/(0.2% offset) | 45 [310] | |
| Elongation in 8 in. [200mm], min % | ... | |
| Elongation in 2 in. [50mm], min, % | 18 | |
| Reduction of area, min % | 45 (measured on round specimen) 40 (measured on flat specifmen) |
|
Chemical Requirements
| Element | Chemical Composition (%) inc. Grade & UNS No. | |
| Grade 22 (UNS: K21590) | ||
| Carbon: | ||
| Heat Analysis: | 0.05 - 0.15 | |
| Product Analysis: | 0.04 - 0.15 | |
| Manganese: | ||
| Heat Analysis: | 0.30 - 0.60 | |
| Product Analysis: | 0.25 - 0.66 | |
| Phosphorus: | ||
| Heat Analysis: | 0.035 | |
| Product Analysis: | 0.035 | |
| Sulphur (max): | ||
| Heat Analysis: | 0.035 | |
| Product Analysis: | 0.035 | |
| Silicon: | ||
| Heat Analysis: | 0.50 max | |
| Product Analysis: | 0.50 max | |
| Chromium: | ||
| Heat Analysis: | 2.00 - 2.50 | |
| Product Analysis: | 1.88 - 2.62 | |
| Molybdenum: | ||
| Heat Analysis: | 0.90 - 1.10 | |
| Product Analysis: | 0.85 - 1.15 | |
Tension Test Requirements:
The material shall be tested using a test specimen will confirm to the tensile requirements as outlined in Table 2.Other requirements:
The following requirements and testing procedures (which are not mandatory) are considered suitable for Chrome Molybdenum steel:- Vacuum treatment
- Product Analysis
- Additional Tension Test
- Charpy V-Notch Impact Test
- Drop Weight Test
- High Temperature Tension Test
- Ultrasonic Examination
- Magnetic Particle Examination
Steel Product Range:
pressure vessel steel | boiler plate | chrome moly steel | clad plates | structural steel | hic steel
wear resistant steel | stainless steel | heat resistant steel | structural steel sections | pipes/tubulars
hot rolled plate | weather resistant steel
"the solution to your steel requirements"